Yiziphi Izitini Ezingavuthi Ezisetshenziswa Ezitsheni Zokushisa? Umhlahlandlela Ophelele

Izitini zobumba lomlilo yizona ezisetshenziswa kakhulu eziyisisekelo zokungaguquki ezitsheni zokushisa. Zenziwe nge-kaolin cishe30% Al₂O₃, zinokumelana okuhle kakhulu nokushisa kanye nezindleko eziphansi, okwenza zifaneleke kakhulu ezindaweni ezinokushisa okuphakathi(1200–1400℃)njengezindonga zesithando somlilo, amapayipi omoya, kanye nezingxenye zesithando somlilo ezisezingeni eliphansi lokushisa. Ukuzinza kwazo okuhle kokushisa kuvimbela ukuqhekeka ekushintsheni kwezinga lokushisa okusheshayo, kuyilapho ukukwazi kwazo ukukhokhela kusiza ukulawula izindleko zephrojekthi iyonke, okwenza kube ukukhetha okungabizi kakhulu kwezithando zomlilo zezimboni ezivamile.

Izitini ze-alumina ephezulu ziyizindlela ezithuthukisiwe esikhundleni sezitini zobumba olucibilikayo, eziqukethe ngaphezulu48% Al₂O₃. Ngokuphikiswa okuphezulu(1400–1600℃), amandla angcono okucindezela, kanye nokumelana nokuguguleka okunamandla, zifanele izingxenye ezithwala ukushisa okuphezulu njengezintambo zesithando, iziqongo zesithando, kanye neminyango yesithando. Zihlukaniswe ngokuqukethwe kwe-Al₂O₃, zihlangabezana nezidingo ezahlukene zokushisa, okwenza zisetshenziswe kabanzi ezithandweni zokushisa zensimbi kanye nezamakhemikhali lapho kudingeka khona ukuzinza kokushisa okuphezulu.

Izitini ze-silica, ezineOkuqukethwe kwe-SiO₂ okungaphezu kuka-94%, i-excel ekuzinzeni kwevolumu yokushisa okuphezulu, kanye nokushisa okuthambisa umthwalo okungaphezu1650℃Zisetshenziswa kakhulu ezingxenyeni ezishisa kakhulu njengeziqongo zomlilo kanye nama-regenerator, ikakhulukazi ezindaweni zomlilo ezifudumeza umoya. Kodwa-ke, ukumelana kwazo nokushisa okungekuhle kunciphisa ukusetshenziswa kwazo ezindaweni ezinokuguquguquka okuvamile kokushisa.

Izitini ezinamathelayo ze-alkaline, okuhlanganisa izitini ze-magnesia kanye nezitini ze-magnesia-alumina, zenzelwe izindawo ezilukhuni. Izitini ze-magnesia, ezakhiwe kakhulu yi-I-MgO, ingamelana namazinga okushisa afinyelela ku-2000℃futhi zinokumelana okunamandla ne-alkaline slag, okwenza zifanelekele phansi kwesithando kanye nemigqa ye-slag lapho zithintana ne-alkaline melts. Izitini ze-Magnesia-alumina zithuthukisa ukumelana nokushisa ngokwengeza i-alumina, zivumelane nezimo zokusebenza eziyinkimbinkimbi.

Izitini ezikhethekile eziphikisayo njengezitini ze-corundum(Al₂O₃ ≥90%)kanye nezitini ze-silicon carbide zisetshenziselwa izingxenye ezibalulekile. Izitini ze-Corundum zimelana namazinga okushisa angaphezu kwalokhu1800℃futhi zilungele izindawo ezivezwe ngqo emalangabi noma ukuguguleka okukhulu kwe-slag. Izitini ze-silicon carbide zinikeza ukumelana okuhle kakhulu nokuguguleka kanye nokumelana nokushaqeka kokushisa, zifanelekela phansi kwesithando, amapayipi omoya, nezinye izingxenye eziguguleka kakhulu.